摘 要:以天然鳞片石墨为原料制备氧化石墨烯(GO),通过Zn将其还原为石墨烯(RGO),并且生成的ZnO附着在RGO表面。采用XRD、SEM、FTIR、Raman、TEM和矢量网络分析仪(VNA)研究了不同还原温度对所制备的ZnO/RGO复合材料的形貌、结构、氧化程度、电磁损耗特性、德拜弛豫模型及电磁响应行为的影响。结果表明:还原温度为50℃,RGO还原后结构更加完整,层间距为0.89 nm,ZnO/RGO复合材料的介电常数和磁导率均较高,在17.15 GHz达到-41.2 dB,反射损耗小于-10 dB的带宽为3.67 GHz。
关键词:石墨烯,电磁响应行为,氧化石墨烯,自组装,复合材料
Abstract: The graphene oxide (GO) was preparaed by natural flake graphite, then it was reduced to graphene by Zn. ZnO is attached to the surface of graphene. The structure, morphology, degree of oxidation, electromagnetic loss properties and Debye relaxation and microwave absorbing properties of ZnO/RGO composite were investigated by XRD, Raman spectrometer, SEM, TEM, FTIR and Vector network analyzer(VNA). The results show that when the reduction temperature is 50℃ , the structure of graphene is more complete after reduction and the layer spacing is 0.89 nm, the permittivity and permeability of ZnO/RGO composite are higher than graphene oxide. At 17.15 GHz, the reflectivity of ZnO/RGO composite is -41.2 dB, the bandwidth of the reflection loss of ZnO/graphene composite below -10 dB is 3.67 GHz.
Keywords: graphene; electromagnetic response behavior; graphene oxide; self-assembly; composites
作者:马志军等,辽宁工程技术大学 矿业学院,辽宁 阜新
通讯作者:马志军,辽宁工程技术大学 矿业学院,辽宁 阜新
全文详见中国知网学术期刊优先数字出版。
来源:CSCM_OFFICE 中国复合材料学会
原文链接:https://mp.weixin.qq.com/s?__biz=MjM5MTA2NTk1Nw==&mid=2654408545&idx=4&sn=07be0facf7ad9a0766323fffa9eccda4&scene=0#wechat_redirect
版权声明:除非特别注明,本站所载内容来源于互联网、微信公众号等公开渠道,不代表本站观点,仅供参考、交流、公益传播之目的。转载的稿件版权归原作者或机构所有,如有侵权,请联系删除。
电话:(010)86409582
邮箱:kejie@scimall.org.cn
基于还原氧化石墨烯,实现高效的低频微波吸收!
纤维素纳米纤丝-还原氧化石墨烯/聚苯胺气凝胶柔性电极复合材料的制备与性能
血浆蛋白+氧化石墨烯能打印人造肌肉
磁性介孔TiO2/氧化石墨烯复合材料的制备及其对U(VI)的吸附
垂直输运的氧化石墨烯实现高效的盐差能转化
前沿 | 氨基化氧化石墨烯在水性防腐防火一体化涂料中的应用
2分钟实现石墨氧化 石墨烯制备取得重要进展
揭示氧化石墨烯表面水分子介入的质子传导机制
氧化石墨烯可为杀虫剂增效
放射性核素诱导氧化石墨烯团聚机理研究取得进展----中国科学院